In this research, an experimental study was conducted to evaluate the effect of recycled concrete aggregate on the characteristics of the concrete produced from it, such as compressive strength, splitting tensile strength and modulus of elasticity, when used in different ratios (0%, 25%, 50%, 75%, 100%) With and without the pozzolanic additions, which were used as an addition to the concrete mixture of 15% cement weight. The research also provided for an experimental relationship to calculate the modulus of elasticity of a concrete produced from recycled aggregate, which demonstrated the comparisons made the possibility of using it for this type of concrete is much nearer to the experimental values of the modulus of elasticity.

В этом исследовании было проведено экспериментальное исследование для оценки влияния переработанного бетонного заполнителя на характеристики получаемого из него бетона, такие как прочность на сжатие, прочность на растяжение при растяжении и модуль упругости при использовании в разных соотношениях (0%, 25 %, 50%, 75%, 100%) С добавлением пуццоланина и без него, которые использовались в качестве добавки к бетонной смеси с содержанием цемента 15%. Исследование также обеспечило экспериментальную зависимость для расчета модуля упругости бетона, полученного из рециркулированного заполнителя, который показал, что сравнения позволили использовать его для этого типа бетона намного ближе к экспериментальным значениям модуля упругости.