The article discusses the use of nano-cement (NCA), which was obtained by the method of chemical deposition from the gas phase. Testing of the cement materials was performed by the traditional destructive method and also using special ultrasonic equipment. Samples of nuts were tested for compressive strength and tension. The results showed that the use of the NCA will have an insignificant effect on strength characteristics, while the results of other research groups show that NAC significantly improves the properties of cement. The hypothesis that the characteristics of the modified pasty matrix NCA strongly depend on the geometric characteristics of the nanofibers, such as length, structure type (single-layer, multi-walled) and chirality.
Рассмотрено использование наноуглеродного цемента (НУЦ), который был получен методом химического осаждения из газовой фазы. Испытания цементных материалов проводились традиционным разрушающим методом, а также с использованием специального ультразвукового оборудования. Образцы с НУЦ испытывали на прочность при сжатии и растяжении. Результаты показали, что использование НУЦ оказывает незначительное влияние на прочностные характеристики, в то время как результаты других исследовательских групп показывают, что НУЦ значительно улучшает свойства цемента. Выдвинута гипотеза о том, что характеристики модифицированной пастообразной матрицы НУЦ сильно зависят от геометрических характеристик нановолокна, таких как длина, тип структуры (однослойные, многостенные) и хиральность.
Document access rights
| Network | User group | Action | ||||
|---|---|---|---|---|---|---|
| ILC SPbPU Local Network | All |
|
||||
|
Internet | All |
|
Included in
Usage statistics
|
|
Access count: 486
Last 30 days: 13 Detailed usage statistics |