The relaxation processes in high-impact polystyrene (HIPS) films filled with titanium dioxide (TiO[2]) of the rutile modification have been investigated by means of dielectric relaxation spectroscopy (DRS) supplemented by differential scanning calorimetry (DSC). Films with 2, 4, 6 and 8 vol.% TiO[2] were compared to each other and to unfilled samples. Above the glass transition one relaxation became visible for unfilled HIPS. It could be identified as the relaxation, related to the onset of micro-Brownian motions at the glass transition. The low-frequency (LF) process (which superimposed with relaxation near Tg) was observed in all TiO[2] containing films. The LF process for composite films was not uniform and showed Arrhenius behavior. At lower temperatures (up to about 130 C) an activation energy of 1.1 eV was found, whereas in the limit of high temperatures, and particularly for higher TiO[2] content the activation energy was 2.4 eV.
Методом диэлектрической спектроскопии проведено исследование релаксационных процессов в композитных пленках на основе ударопрочного полистирола (УПС) с диоксидом титана TiO[2] в качестве наполнителя. Сравнивалось поведение пленок УПС без наполнителя и композитных пленок с разным содержанием TiO[2] (2, 4, 6 и 8 об.%). Для пленок УПС без наполнителя установлено наличие одного релаксационного процесса (альфа-релаксация). Для композитных пленок обнаружен неоднородный низкочастотный релаксационный процесс, подчиняющийся закону Аррениуса. Значения энергии активации, рассчитанные для низких (до 130 С) и высоких (свыше 130 С) температур, составили 1,1 и 2,4 эВ, соответственно.
Included in
Usage statistics
Access count: 0
Last 30 days: 0 Detailed usage statistics |