Аннотация
It is known that polymer films based on a copolymer of polyvinylidene fluoride and tetrafluoroethylene P(VDF-TFE) have piezoelectric properties, and these properties appear only after preliminary stretching of the films. The polar crystalline beta-phase of the copolymer is responsible for the piezoelectric properties in the P(VDF-TFE), the percentage of this phase in the polymer can vary. In this work, we have studied the influence of the orientational stretching rate on the stability of the electret, and, as a consequence, the piezoelectric state. The influence of rheological parameters on the polymer structure and the parameters of electrically active defects responsible for polarization processes is shown.
Известно, что полимерные пленки на основе сополимера поливинилиденфторида и тетрафторэтилена П(ВДФ-ТФЭ) обладают пьезоэлектрическими свойствами, причем эти свойства проявляются лишь после предварительной вытяжки пленок. За пьезоэлектрические свойства в П(ВДФ-ТФЭ) отвечает полярная кристаллическая бета-фаза сополимера, процентное содержание которой в полимере может варьироваться. В данной работе исследовано воздействие скорости ориентационной вытяжки на стабильность электретного, и, как следствие, пьезоэлектрического состояния. Показано влияние реологических параметров на структуру данного полимера и параметры электрически активных дефектов, ответственных за процессы поляризации.
Права на использование объекта хранения
| Место доступа | Группа пользователей | Действие | ||||
|---|---|---|---|---|---|---|
| Локальная сеть ИБК СПбПУ | Все |
|
||||
|
Интернет | Все |
|
Входит в состав
Статистика использования
|
|
Количество обращений: 257
За последние 30 дней: 12 Подробная статистика |