- EVALUATION OF DAMAGE INDUCED IN GRAPHITE DUE TO SAMPLE PREPARATION BY STANDARD NON-DESTRUCTIVE TECHNIQUES
- Michael Lasithiotakis1*, James T. Marrow2, Barry J. Marsden3
- 1Greek Atomic Energy Commission, P.O BOX 60092, P.C. 15341, Agia Paraskevi – Athens, Greece
- 2Department of Materials, University of Oxford, Parks Road, Oxford OX1 3PH, UK
- 1. Introduction
- 2. Methods
- Gilsocarbon Polycrystalline Graphite Preparation: Mechanical Polishing and Fracturing. Gilsocarbon polycrystalline graphite surfaces were prepared by simple manual polishing on a metallographic grinding wheel, operated at 200 rpm with tap water as a c...
- Highly Oriented Pyrolytic Graphite (HOPG) Preparation. A specimen of Highly Oriented Pyrolytic Graphite (HOPG) [26,27] produced by SPI Supplies U.S.A and measuring approximately 1 cm × 1 cm × 0.1 cm, was cold mounted in resin and cut into pieces of 3...
- BEPO Graphite - Occurrence, Sampling, and Preparation. Samples of neutron irradiated polycrystalline graphite from British Experimental Pile Zero (BEPO) were obtained from the United Kingdom Atomic Energy Authority (UKAEA), with permission from the UK...
- Ion Beam Irradiation – Method. Ion beam polishing of Gilsocarbon and HOPG specimens was achieved using a precision ion polishing system (Gatan – PIPS), which is designed to prepare specimens for TEM. Two argon beams from opposing directions with a ma...