Recycling of industrial wastes like fly ash into construction materials is attaining more momentum nowadays towards enhancing the characteristics and performance of materials in terms of strength and durability. This article attempts to present the effect of fly ash inclusion on the properties of bricks through a comparative feasibility analysis of fly ash bricks (FB), clay bricks (CB), and fly ash incorporated clay bricks (FC). For experimentation, twelve brick specimens were made using fly ash, clay, lime, gypsum, sand, and water in different proportions followed by sun-drying and firing methods. Sieve analysis, X-ray diffraction (XRD), Scanning electron microscope (SEM), Energy Dispersive X-ray Fluorescence (EDXRF), Fourier-transform infrared spectroscopy (FTIR), compressive strength, and efflorescence tests were performed to study the properties of brick specimens. Various factors such as the effect of drying, heating temperature, and percentage of ash addition on the bricks were also observed. The laboratory results indicated that out of the above-mentioned three bricks, FB showed better performance than CB and FC. The compressive strength and water absorption values for FB were found in the range of 8.50–12.18 MPa and 10.84–13.11 %, respectively. Thus, based on the experimental observations and results, the mix design FB-3 (25 % fly ash, 20 % lime, 2 % gypsum, 53 % sand) exhibited the optimum compressive strength of 10.25 MPa with a water absorption value of 11.16 %. This mix design can be recommended as a substitute for conventional bricks against aggressive environment contributing immensely towards solid waste management and sustainable development.

• Comparative feasibility analysis of fly ash bricks, clay bricks and fly ash incorporated clay bricks
  • 1. Introduction
  • 2. Methods
    • 2.1. Raw materials
    • 2.2. Fabrication of brick specimens
    • 2.3. Testing Methods
  • 3. Results and Discussion
    • 3.1. Characterization of Raw materials
• 3.1.1. Sieve analysis
• 3.1.2. Chemical analysis
• 3.1.4. FTIR analysis of fly ash and clay
  • 3.2. Mechanical properties
• 3.2.1. Compressive strength and water absorption
  • 3.3. Effect of various parameters on brick specimens
• 3.3.2. Effect of firing temperature on CB strength properties
• 3.3.3. Effect of ash content on FC strength properties
  • 3.4. Efflorescence test of FB, CB and FC
  • 3.5. Effect of firing process on colour of CB
  • 3.6. Works by other authors
  • 4. Conclusions

Magazine of Civil Engineering / Санкт-Петербургский политехнический университет Петра Великого. — Санкт-Петербург: СПбПУ, 2020-. — Периодичность: 8 раз в год. — Выходит с 2020 г. — Загл. с титул. экрана. — Свободный доступ из сети Интернет (чтение, печать, копирование). — Электрон. журнал. — Текст: электронный