In the paper, polycrystalline copper deformed by tension under different conditions of loading has been studied using electron backscatter diffraction. The microstructure of areas located on the longitudinal section of the specimens deformed until fracture was examined. The fragmentation of initial grains in case of deformation at room temperature was observed whereas at 400 С, considerable dynamic recovery and recrystallization significantly influenced the microstructure formation. A procedure for computer analysis of the orientation maps has been put forward, which allows separating recrystallized regions from the non-recrystallized ones and further analyzing the misorientation statistics of strain-induced boundaries. A scaling behavior of the strain-induced misorientation distributions was shown to take place. The mechanism of strain-induced boundary evolution was proved to remain unchanged for all studied deformation conditions, in spite of recovery and recrystallization occurring at elevated temperatures.

В работе исследована поликристаллическая медь, деформированная растяжением в различных условиях (использован метод дифракции обратнорассеянных электронов). Проанализирована микроструктура участков, расположенных на продольном сечении образцов, деформированных до разрушения. В случае деформации при комнатной температуре, наблюдали фрагментацию исходных зерен, тогда как при 400 С на формирование микроструктуры значительное влияние оказывали динамический возврат и рекристаллизация. Предложена процедура компьютерного анализа ориентационных карт, позволяющая отделять рекристаллизованные области от нерекристаллизованных и анализировать статистику разориентировок на границах деформационного происхождения. Доказано, что механизм эволюции разориентировок остается неизменным для всех изученных условий деформации, несмотря на динамический возврат и рекристаллизацию при повышенной температуре.