The work studies regularities of the formation of wedge-shaped twins under growing concentrated load in single crystals of bismuth, zinc and bismuth-antimony alloy. It was established that the twinning, detwinning and stopping of the twin deformation near the stress concentrator can take place simultaneously with the load growth. Reversibility of plastic deformation during twinning in metals at the stage of residual twinning development were discovered. Various manifestations of spontaneous detwinning of wedge-shaped twins which emerge at stress concentrators when indenting Bi, Zn, Bi-Sb single crystals with increasing load are quantitatively studied. Depending on the value and the sign, local fields of elastic stress can encourage or discourage twinning, or cause detwinning.
Изучены закономерности формирования клиновидной сдвойникованной области в монокристаллах Bi, Zn и сплава Bi-Sb под действием возрастающей сосредоточенной нагрузки. Установлено, что изменение размеров остаточного клиновидного двойника с ростом нагрузки может происходить по одному из десяти вариантов, в которых длина двойника и его ширина у устья либо увеличиваются, либо уменьшаются, либо остаются неизменными в разных сочетаниях. Локальные поля упругих напряжений в зависимости от величины и знака могут стимулировать двойникование, препятствовать ему или вызывать раздвойникование. Обнаруженное явление самопроизвольного раздвойникования клиновидных двойников в металлах при увеличении внешних механических напряжений свидетельствует о том, что обратимость пластической деформации при двойниковании есть фундаментальное свойство этого вида деформации и проявляется не только при упругом двойниковании, но и на стадии остаточного двойникования.
Usage statistics
Access count: 495
Last 30 days: 6 Detailed usage statistics |