The structural instability of Fe-Cr-Ni-based superalloys and the mechanism of softening at operating temperatures were studied. We investigated the continuous changes in the structure and kinetics of dissolution of initial phases with formation and dissolution of intermediate phases of the cast superalloy 0,45C-26Cr-33Ni-2Si-2Nb under long-time operation at high temperature. The character and the sequence of phase transformations in Fe-Cr-Ni-based alloys at a temperature of 0,85-0,90 of their solidus, also under external loading, were found out. The structural instability of Fe-Cr-Ni-based superalloys and the mechanism of softening at operating temperatures were studied.

Изучены структурная нестабильность и механизм разупрочнения при температурах эксплуатации жаропрочных сплавов на основе системы Fe-Cr-Ni. Исследованы непрерывные изменения структуры и кинетика растворения первичных фаз с образованием и последующим растворением промежуточных фаз в литом жаропрочном сплаве 0,45C-26Cr-33Ni-2Si-2Nb при длительной высокотемпературной эксплуатации. Выявлены характер и природа фазовых превращений в сплавах на основе системы Fe-Cr-Ni при температурах 0,85-0,90 от температуры солидус, а также под действием внешней нагрузки. Изучены структурная нестабильность и механизм разупрочнения жаропрочных сплавов на основе системы Fe-Cr-Ni при температурах эксплуатации.

Научно-технические ведомости СПбГПУ. — Санкт-Петербург: Изд-во СПбГПУ, 1995- № 3 (249) [Электронный ресурс]. — Электрон. текстовые дан. (1 файл : 23,9 МБ). — Санкт-Петербург: Изд-во Политехн. ун-та, 2016. — Загл. с титул. экрана. — Электронная версия печатной публикации. — Свободный доступ из сети Интернет (чтение, печать, копирование). — Текстовый документ. — Adobe Acrobat Reader 7.0. — <URL:http://elib.spbstu.ru/dl/2/j17-52.pdf>.