Details

The results of complex researches on studying of influence of parameters of particulate reinforcement and the material of the fibers on the strength of the disperse-reinforced fine-grained concrete on a stretching at a bend, the estimation of efficiency and accountability in the calculation of building structures. It is proved that a coarser texture leads to a greater bonding force between the filler particles and the cement matrix. The questions of application of steel fiber for dispersed reinforcement of fine-grained concrete are considered. As a binder, thin-milled cement and binders of low water demand were used. To increase the strength and deformation characteristics, the compositions of fine-grained fiber concrete on technogenic raw materials and composite binders with the use of nanodispersed powder were developed. It is established that the use of composite binders and high-density packing of filler grains significantly increase the strength characteristics.

Представлены результаты комплексных исследований по изучению влияния параметров дисперсного армирования и материала волокон на прочность дисперсно-армированного мелкозернистого бетона на растяжение при изгибе, дана оценка эффективности такого метода и возможность учета при расчете строительных конструкций. Доказано, что более грубая текстура приводит к большей силе сцепления между частицами заполнителя и цементной матрицей. Рассмотрены вопросы применения стальной фибры для дисперсного армирования мелкозернистых бетонов. В качестве вяжущего использовался тонкомолотый цемент и вяжущее низкой водопотребности. Для увеличения прочностных и деформативных характеристик были разработаны составы мелкозернистого фибробетона на техногенном сырье и композиционных вяжущих с применением нанодисперсного порошка. Установлено, что применение композиционных вяжущих и высокоплотной упаковки зерен заполнителя значительно повышают прочностные показатели.